PROPERTIES1 |
METHOD OR CONDITIONS |
PARYLENE C |
EPOXIES2 |
SILICONES2 |
URETHANES2 |
Secant modulus, psi |
ASTM D882-56T @ 1% strain |
400,000 |
350,000 |
900 |
1,000-10,000 |
Tensile strength, psi |
ASTM D882-56T @ 10% strain/min |
10,000 |
4,000-13,000 |
800-1000 |
175-10,000 |
Yield strength, psi |
ASTM D882-56T @ 10% strain/min |
8,000 |
|
|
|
Elongation to break, % |
ASTM D882-56T @ 10% strain/min |
200 |
3-6 |
100 |
100-1,000 |
Yield elongation, % |
ASTM D882-56T @ 10% strain/min |
2.9 |
|
|
|
Density, gm/cc |
ASTM D1505-57T |
1.289 |
1.11-1.40 |
1.05-1.23 |
1.10-2.5 |
Index of refraction, N 23 |
Abbe refractometer |
1.639 |
1.55-1.61 |
1.43 |
1.50-1.60 |
Water absorption, 24 hrs |
ASTM D570-57T |
0.06 |
0.08-0.15 |
12 (7 days) |
0.02-1.5 |
Rockwell hardness |
ASTM D785-65 |
R80 |
M80-M110 |
40-45 (shore A) |
10A-230 (shore) |
Coefficient of friction: |
ASTM D1894-63 |
|
 Static
|
0.29 |
|
|
|
Dynamic |
0.29 |
|
|
|
|
|
1.Properties measured on parylene films, 0.001-.0003 inch thick, except where specified.
2.Properties depend somewhat on deposition conditions.
|